7 Jun 2010: 5. To conclude, some socio-economic aspects related to this programme can be outlined. ... From the socio-economic point of view, it can be said that steel construction captures economic and environmental goals with social desirability.

7 Jun 2010: The hydrogen embrittlement susceptibility of the steels was evaluated by means of a constant loading test, a slow strain rate test and a hydrogen immersion test. ... For the CLT, the constant load was applied to samples with a conventional creep test

7 Jun 2010: Tests were carried out in accordance with JIS Z 3158 [7]; 60mm anchorage welds were made at either end of the 80mm test section using a GMAW procedure with AWS ER ... For the wide plate tests the stresses were estimated from the test records as force

7 Jun 2010: Charpy V Notch Charpy V Notch impact test impact test. (CVN)(CVN). ... SMAW FCAW SAWE= 12kJ/cm E= 8 kJ/cm E= 35 kJ/cm. Bent test after welding : A913/gr.

7 Jun 2010: The delaminations lead to a decrease in triaxiality of the stress state in the impact test samples. ... Impact tests were conducted in a temperature range from 103 to 423 K.

7 Jun 2010: The fatigue limit (obtained by HCF test) was slightly higher in welded normalized steel than in welded TMCP steel. ... Vickers hardness test was made under a 300 g load along a line crossing base metal, HAZ and weld metal.

7 Jun 2010: Specimens for torsion tests, 10 mm in diameter with a gauge length of 15 mm, were machined from the ingots. ... CONCLUSION The hot workability of three different ingots of P91 steel was investigated by means of monotonic torsion tests.

7 Jun 2010: Slow speed tensile tests were made (0.8 mm/min) 1 hour and 1 week after pickling. ... Thickness. mm. Test type Method / arc energy. kJ/mm. ReH/p0.2. N/mm2.

7 Jun 2010: After austenitisation (900 C for 600 s), the following dilatometric tests have been carried out:. ... 11) constituted of 96%-92% ferrite and 4%-8% MA, confirming the results obtained with the dilatometric tests.

7 Jun 2010: Figure 7. Some results of crossweld creep tests on a SA weld in P23. ... The total test duration was 4.000h with intervals after 500,1.000 and 2.000h.