Search. Dissemination of IT for the Promotion of Materials Science (DoITPoMS). Full Record for Micrograph 397. Full Record for Micrograph 397. [183 KB]. You can also view and download the micrographs on Flickr.. Micrograph no. 397. Brief

Length bar. 200 μm. Further information. A good example of the creation of annealing twins.

Length bar. 200 μm. Further information. A medium carbon steel that has been quenched producing martensite laths in the microstructure.

Length bar. 200 nm. Further information. Spherical particles of polystyrene, with a mean diameter of 144 nm, and about a 10% standard deviation in particle size.

Length bar. 200 μm. Further information. Medium carbon steel that has been slow quenched, and resulting in the production of Widmanstätten ferrite.

Length bar. 200 μm. Further information. A cast iron with a relatively low carbon content.

200 μm. Al 96, Cu 4 (wt%), solution treated and overaged - precipitation hardening. ... 200 μm. Fe, C 2, Mn 0.7 (wt%) steel, quenched, producing martensite and cracking.

200 μm. Cu 80, Sn 20 (wt%) bronze, as cast. System: Cu-Sn, Composition: Cu 80, Sn 20 (wt%). ... 200 μm. Cu 80, Sn 20 (wt%) bronze, exhibiting dendritic solidification.

Scanning electron microscopy (SEM) in backscattered electron imaging (BEI) mode. 200 μm.

Standard codes. Reaction. Processing. Austenitised at 1000 ºC, quenched into molten salt at 600 ºC , partially transformed, quenched into water at 200 ºC.