Length bar. 200 μm. Further information. An example of a white cast iron, so named due to its relatively low carbon content, which means that the carbon present is in the

Length bar. 200 nm. Further information. A replica of a 3:1 blend of linear with lightly branched polyethylenes (BPE has 26 branched per 1000 backbone carbon atoms) after isothermal crystallisation

Length bar. 200 μm. Further information. An example of a hypereutectoid steel (one that has a carbon composition above that of the eutectic).

Reflected light microscopy. 200 μm. Unidirectional T800 carbon fibres in an MTM49 epoxy matrix. ... System: CCcomposite, Composition: Not specified. Reflected light microscopy. 200 μm. Alumina-graphite brick.

Length bar. 200 μm. Further information. An example of a hypereutectoid steel (one that has a carbon composition above that of the eutectic).

Length bar. 200 μm. Further information. This micrograph is of a specimen which has been pressed from either side during fabrication, with the bright graphite flakes appearing edge on.

Length bar. 200 μm. Further information. This micrograph is of a specimen which has been pressed parallel with your nose (into the screen) during fabrication, with the bright graphite flakes appearing

Length bar. 200 μm. Further information. This sample has the eutectic composition so all the liquid solidifies at the eutectic temperature to form a lamellar eutectic structure.

Length bar. 200 μm. Further information. This sample was quenched to -80 ÂC to give a metastable martensitic microstructure.

200 μm. Cu 70, Zn 30 (wt%), recrystallised - annealing twins. ... 200 μm. Austenitic stainless steel. System: Fe-C-X, Composition: Stainless steel. Reflected light microscopy.