Reflected light microscopy. 200 μm. Whiteheart cast iron. System: Fe-C-X, Composition: Fe, C 3.4, Si 0.35, Mn 0.22 (wt%),. ... Reflected light microscopy. 200 μm. Blackheart cast iron. System: Fe-C-X, Composition: Fe, C 2.4, Si 1.1, Mn 1.1 (wt%).

Length bar. 200 μm. Further information. Low carbon steel with a microstructure consisting mostly of ferrite.

System: Fe-C-X, Composition: Fe, C 0.8 (wt%). Reflected light microscopy. 200 μm.

Length bar. 200 μm. Further information. Low carbon steel with a microstructure consisting mostly of ferrite.

Length bar. 200 μm. Further information. This steel was quenched from the austenite phase field too rapidly for carbon to diffuse out and form cementite.

Length bar. 200 μm. Further information. The steel has been rapidly quenched.

Length bar. 200 μm. Further information. Whiteheart malleable castings are produced from high carbon white cast irons annealed in a decarburising medium.

Reflected light microscopy. 200 μm. MgO-C Refractory Brick. System: MgO-C, Composition: MgO 50-90, C 8-37 (wt%), remainder Al, Si metal addition. ... Reflected light microscopy. 200 μm. Grey cast iron (flake graphite). System: Fe-C-X, Composition: Fe,

Length bar. 200 μm. Further information. An example of a white cast iron, so named due to its relatively low carbon content, which means that the carbon present is in the

Length bar. 200 μm. Further information. This is an example of a quenched and tempered steel.

Length bar. 200 nm. Further information. A replica of a 3:1 blend of linear with lightly branched polyethylenes (BPE has 26 branched per 1000 backbone carbon atoms) after isothermal crystallisation

Length bar. 200 μm. Further information. An example of a hypereutectoid steel (one that has a carbon composition above that of the eutectic).

Length bar. 200 μm. Further information. An example of a hypereutectoid steel (one that has a carbon composition above that of the eutectic).

Reflected light microscopy. 200 μm. Unidirectional T800 carbon fibres in an MTM49 epoxy matrix. ... System: CCcomposite, Composition: Not specified. Reflected light microscopy. 200 μm. Alumina-graphite brick.

Length bar. 200 μm. Further information. This micrograph is of a specimen which has been pressed from either side during fabrication, with the bright graphite flakes appearing edge on.

Length bar. 200 μm. Further information. This micrograph is of a specimen which has been pressed parallel with your nose (into the screen) during fabrication, with the bright graphite flakes appearing

Length bar. 200 μm. Further information. This sample has the eutectic composition so all the liquid solidifies at the eutectic temperature to form a lamellar eutectic structure.

Length bar. 200 μm. Further information. This sample was quenched to -80 ÂC to give a metastable martensitic microstructure.

Length bar. 200 μm. Further information. Contributor.

System: Polyethylene (PE), Composition: LPE:BPE 1:3. Transmission electron microscopy (TEM). 200 nm. ... Transmission electron microscopy (TEM). 200 nm. Multi-walled carbon nanotube. System: Carbon nanotube, Composition: Not specified.