21 May 2014: Heat Treatment Vickers hardness. 930 C 1h, air cooled to 200 C, held for 10 days, air cooled 622 13. ... Constant-depth nanoindentation was therefore used to tocharacterised changes on cross sections of the wear samples, prepared by polishing with 200

16 Dec 2014: Therefore, over thegrain size (measured as a mean lineal intercept) range relevant in the presentwork, 100 – 200 µm in Fig.

24 May 2014: Hydrogen diusion and thepercolation of austenite in. nanostructured bainitic steel. AUTHORS:Lucy Fielding a (corresponding author)Eun Ju Song b. Do-Kyeong Han b. Harshad Bhadeshia a,b. Dong-Woo Suh b. a Department of Materials Science and

23 Jul 2014: Integrated intensities of (200)α, (211)α, and (220)γ,(311)γ peaks were used for the evaluation of austenite fraction.

26 Jan 2014: 4b. (a) (b). Figure 4: Data for all textures for a stress of 200 MPa applied along the z-axis.

25 Nov 2014: Preprint submitted to Elsevier November 12, 2014. Journal of Magnetism and Magnetic Materials 378 (2015) 200-205. ... Samples were observed ina JEOL 200 CX with an accelerating voltage of 200 kV.

29 Mar 2014: 200. 400. 600. 800. 1000. Load. (µN. ). Displacement (nm). Non-charged H-charged. ... 0 50 100 150 200 2502.5. 2.8. 3.1. 3.4. 3.7. 4.0.

24 May 2014: for different cooling rates assuming zero and 200 J mol1 stored energy contributing to the chemical free energy change. ... steel for different cooling rates assuming zero and 200 J mol1 stored energy contributing to the chemical free energy change.

1 Jul 2014: Due to the tensile stresses developed in the weld metal for weld 4 andthe compression (-200 MPa) in the same region for weld 1 (low MS filler), it.

16 Mar 2014: This sample was taken from a forged production com-ponent, which had been cast as part of a 200-tonne ingot.